[1]张翔,瞿婷婷,田冲,等.注水井口闸门阀杆断裂原因分析[J].石油管材与仪器,2018,4(03):42-45.[doi:10.19459/j.cnki.61-1500/te.2018.03.011]
             ZHANG Xiang,QU Tingting,TIAN Chong,et al.Analysis on Fracture Cause of Screw of Water Injection Well Valve Stem[J].Petroleum Tubular Goods & Instruments,2018,4(03):42-45.[doi:10.19459/j.cnki.61-1500/te.2018.03.011]
            点击复制

            注水井口闸门阀杆断裂原因分析
            分享到:

            《石油管材与仪器》[ISSN:2096-0077/CN:61-1500/TE]

            卷:
            4
            期数:
            2018年03期
            页码:
            42-45
            栏目:
            失效分析与预防
            出版日期:
            2018-06-20

            文章信息/Info

            Title:
            Analysis on Fracture Cause of Screw of Water Injection Well Valve Stem
            文章编号:
            2096-0077(2018)03-0042-04
            作者:
            张翔1瞿婷婷1田冲2蔡克1陈志昕1
            1.中国石油集团石油管工程技术研究院 陕西 西安 710077;2.甘肃蓝科石化高新装备股份有限公司 甘肃 兰州 730070
            Author(s):
            ZHANG Xiang1 QU Tingting1 TIAN Chong2 CAI Ke1 CHEN Zhixin1
            1. CNPC Tubular Goods Research Institute, Xi′an, Shaanxi 710077, China; 2. Lanpec Technologies Limited, Lanzhou, Gansu 730070, China
            关键词:
            闸门晶粒裂纹
            Keywords:
            valve grain crack
            分类号:
            TE931
            DOI:
            10.19459/j.cnki.61-1500/te.2018.03.011
            文献标志码:
            A
            摘要:
            通过化学成分分析、夏比冲击、金相分析和能谱分析等,分析了注水井闸门阀杆断裂失效的原因。结果表明,闸门阀杆材料为Cu-Zn合金,Zn、Pb、Fe、Sn、Al、Ni元素含量不符合标准要求,组织晶粒粗大,材?#20808;?#24615;差,裂纹在台肩处形成并沿晶界扩展,直至断裂,即阀杆材料质量不合格是造成断裂失效事故的主要原因。
            Abstract:
            The reason for the valve stem fracture is analyzed through chemical composition analysis, Charpy impact text, EDS and so on, the results show that the material of the valve stem is CuZn alloy. Meanwhile, the elements content of Zn, Pb, Fe, Sn, Al and Ni do not conform to the standard requirements, the coarse grains and the poor toughness of the valve stem material lead to the formation of cracks along the shoulder grain boundaries expanding to the nut heart until it breaks, it is that the unqualified valve stem material is the main cause of fracture failure.

            参考文献/References:

            [1] 彭小强,刘先印,吴虎.新疆油田冷冻井口带压更换闸技术的研究与应用[J].新疆石油科技,2014,24(2):36-41.
            [2] 冉俊义,成斌,张志强,等.注水井采油树闸门拆卸工具的研制与应用[J].河北企业,2017,9:161-162.
            [3] 宋宝玉,张立鹤,聂连雨,等.注水井带压更换井口阀门工艺技术研究[J].科技与企业,2014,6:188.
            [4] 张文龙,郭煜,石玉辉,等.注水井带压更换井口阀门技术应用[J].内蒙古石油化工,2010,18:79-82.
            [5] 田玉琛,谢平,陈磊,等.利用可捞式油管桥塞不压井更换井口闸门技术[J].断块油气田,2009,16(4):118-120.
            [6] 宋?#34013;?郭振三,杨磊.关于注水井套管主控闸门带压更换技术应用探讨[J].黑龙江科技信息,2017(6):77.
            [7] 张鸣,伍超群,李扬.铅黄铜阀体开裂原因分析[J].材料研究与应用,2009,3(3):200-203.
            [8] 刘柏雄,张?#30655;?Sn对易切削Bi黄铜组织及性能的影响[J].特种铸造及有色合金,2011,31(3):288-290.
            [9] 钱泽涛,王敏,苏华.Sn对H65黄铜组织和性能的影响[J].铜业工程,2016(4):41-44.
            [10] 肖翔鹏,柳瑞清,张英,等.铝对复杂黄铜组织及性能的影响[J].有色金属科学与工程,2014(5):92-96.

            备注/Memo

            备注/Memo:
            第一作者简介:张翔,女,1985年生,工程师,2011年毕业于西安理工大学材料科学与工程专业,获硕士学位,现从事石油管材质量检测及失效分析。E-mail:[email protected]
            更新日期/Last Update: 2018-06-25
            宁夏11选5 9彩票app 胜负彩17059期预测分析 陕西快乐十分最新开奖 王中王四肖中特 免费彩票 大乐透荐号最准专家 吉林十一选五助手软件 上海快3豹子最大遗漏 安徽时时彩结果查询 中原福彩官方手机客户端下载 体彩黑龙江6+1第18090期 半全场开奖结果 快三开奖结果青海今天 pk10一万本金怎样打稳 竞彩足球比分预测网易